Low sodium tabular alumina as filtration Low sodium tabular alumina is of sodium content(Na2O) less than 0.2% even less than0.1%. The Na2O content effect the density, hardness, apperaent porosity. Low sodium means better thermal performance. It enhance the abilities of
The Application of Tabular Alumina Tabular Alumina has good slag resistance, high temperature corrosion and erosion resistance, high specific gravity, high purity, and low apparent porosity. It is suitable for refractory, steel making and foundry. The applications of tabular alumina
Tabular alumina castable features Tabular alumina castable are mainly made of tabular alumina with high purity and high melting point. The tabular alumina castable 220F/325F have high thermal shock stability, anti-stripping and creep resistance. It also featured with high
Tabular corundum for fire bricks High-purity corundum bricks have high density, stable chemical properties, and strong corrosion resistance at high temperatures. They are suitable for refractory parts used in gasifiers and industrial kilns. Fused corundum is always adopted as the
What makes the high quality tabular alumina? High quality tabular alumina make higher quality reliable refractory products such as fire bricks, sliding gate plate,linings,etc. It has to be low porosity, low water absorption and high density. In the manufacturing of
White Tabular Alumina vs. White Fused Alumina The production of fused alumina is a high-energy consumption process. It consumes 2000-3000 kWh of electric power per ton. While the comprehensive energy consumption of white tabular alumina is only 20% to 35%
Crystal structure of sintered tabular alumina Sintered tabular alumina is tabular shape aluminum oxide. The sintering process of tabular alumina is a process of rapid cooling and rapid heating. The sintering temperature rapidly drops from 1950°C to about 400°C. The
Tabular Alumina 325 mesh powder for thermal conductive adhesive Tabular Alumina 325 mesh powder has a particle size range of 0-45 microns. It is of excellent fire resistance, stable thermal performance. It can improve the performance of thermal adhesives.
The advantage of Sintered Tabular Alumina is apparent comparing with Fused Alumina. Sintered Tabular alumina is sintered corundum produced by the process of milling, forming, drying, and sintering high-purity industrial alumina powder as raw material. The sintering process is the
There are tabular alumina refractory castables and tabular alumina refractory aggregate. Generally, tabular alumina specifications are available as follows: Size Distribution Guarantee Value 5-10mm or 1/2-1/4inch +12.5mm 0-2% +10.0mm 1-25% +6.3mm 47-83% -4.0mm 0-2% 3-6mm/3-6#